品名称 Spec. | 规格Size (单位：mm) | 主要标准Standards |
Rod | Forged Rod Φ(26-400)×≤4000 Rolled Rod Φ(5.5-90)×≤9000 | GB/T,GJB,BS,ASTM,ASME,AMS,MIL,JIS |
Disk | OD≤2000，Thk ≥40 | GB/T,GJB,ASTM,AMS |
Ring | OD≤3000，Height≤750 | GB/T,GJB,ASTM,AMS |
Wires | Φ(0.6-5.5)×L | GB/T,GJB,AWS,ASTM,AMS,JIS |
Ti-Cu Clad | Drum; Round, Square, Hollow. | GB/T12769 |
Technical Data Sheet
Chemical Composition Limits | |||||||||
Weight % | Al | Mo | V | Fe | C | N | H | O | Other (total) |
Titanium 8Al-1Mo-1V | 7.35-8.35 | 0.75-1.25 | 0.75-1.25 | 0.30 | 0.08 | 0.05 | 0.015 | 0.15 | 0.40 |
Titanium 8-1-1 (8Al-1Mo-1V) is a near alpha alloy offering good weldability and with superior creep resistance at operating temperature up to 450°C. Alloy 8-1-1 has a relatively high tensile modulus to density ratio and is used primarily in engine applications such as forged compressor blades and disks.
Typical Mechanical Properties
Material | Diameter | Tensile Strength min | Yield Strength | Elongation (%) | Reduction of area(%) | ||
ksi | Mpa | ksi | Mpa | ||||
Titanium 8Al-1Mo-1V Bar Solution treated and stabilized | Up to 2.5" | 130 | 896 | 120 | 827 | 10 | 20 |
Titanium 8Al-1Mo-1V Bar Solution treated and stabilized | 2.5" - 4.0" | 120 | 827 | 110 | 758 | 10 | 20 |
Availability
Titanium (8-1-1) 8Al-1Mo-1V is available in sheet, strip and bar. For all stock and size availability of Titanium 8Al-1Mo-1V contactSales.
Specifications
AMS 4915 sheet, strip, plate (single annealed)
AMS 4916 sheet, strip, plate (duples annealed)
AMS 4972 bar, wire, ring (solution treated and stabilized)
AMS 6910 bar (duplex annealed)
AMS-T-9046 A-4 sheet, strip, plate
AMS-T-9047 8Al-1Mo-1v bar
MIL-T-9046J A-4 sheet, strip, plate
MIL-T-9046H Type II Comp F sheet, strip, plate
MIL-T-9047G 8Al-1Mo-1V bar