home > 钛合金Ti-8-1-1

钛合金8-11

 TABLE 1 

化学成分

ELEMENT 

WEIGHT % 

               Min. 

Max. 

Nominal 

Aluminum 

7.35 

8.3 

7.85 

Vanadium 

0.75 

1.25 

1.0 

Iron 

0.15 

Molybdenum 

0.75 

1.25 

1.0 

Carbon 

0.08 

Nitrogen 

0.05 

Oxygen 

0.06 

0.12 

0.85 

Hydrogen 

0.004 

Residuals (each) 

0.1 

Residuals (total) 

0.3 

 

 TABLE 2 

物理性能

PROPERTY 

VALUE 

                    English 

          SI 

Density 

0.156 lb/in3 

4.37 g/cm3 

Beta Transus 

1900 ± 30 °F 

1040 ± 17 °C 

Tensile Modulus 

Duplex Annealed 1650 ° F /1hr /AC + 1100 ° F/ 24hr / AC 

At 75° F 

19 Msi 

135 GPa 

At 716 °F 

16 Msi 

113 GPa

  

    TABLE 3 热性能 

 

                             

       Temperature,°F(°C)

Electrical Resistivity,

μΩ-cm

Conductivity λ, Btu.ft/h.ft2. °F

(W/m.K)

Coefficient of Thermal Expansion

10-6 in in-1°F-1

(x 10-6mm-1 °C-1)

75

(24)

198.6

3.46

(5.98)

-

200

(93)

201.3

3.94

(6.82)

Temp range 68-212°F: 4.7

(8.46)

400

(204)

202.7

4.76

(8.23)

Temp range 68-392°F: 4.9

(8.82)

600

(315)

201.2

5.64

(9.75)

Temp range 68-572°F: 5.0

(9.00)

800

(427)

201.1

6.48

(11.21)

Temp range 68-7522°F: 5.2

(9.36)

1000

(538)

203.4

7.23

(12.51)

Temp range 68-932°F: 5.4

(9.72)

1200

(649)

206.0

7.98

(13.80)

Temp range 68-1112°F: 6.0

(10.8)