Metal Powder

Aircraft Materials offers a comprehensive range of high-quality metal powders, produced and tested to exacting standards for use in all processes including Additive Manufacturing (AM), Near-Net Shape Powder Metallurgy (NNS/PS) and Hot-Isostatic Pressing (HIP).

Additive Manufacturing (AM)

This refers to the process of producing a part by progressively adding successive layers and forming by way of laser or proton beam. Currently additive manufacturing finds application in many fields including aerospace, aviation, the medical industry, chemical and power generation, defence and automotive. This technology relies on high powder sphericity and specific particle sizes to ensure the final shape and density of the finished part. Powders for additive manufacturing can be supplied in a range of Particle Size Distributions (PSD) to fit the process:

Laser Powder Bed Fusion (L-PBF): 15-45µm

Direct Energy Disposition (DED): 45-150 µm

Electron Beam Melting (EBM): 45-106 µm

Hot Isostatic Pressing (HIP)

Hot Isostatic Pressing is a process in which high pressure, applied by an inert gas (usually argon) is used to improve material properties. Castings which are used in critical applications can also be produced using metal powders as internal defects and internal microporosity are reduced, thus improving mechanical properties. Powdered metal can be used in the HIP process to produce a range of components, from simple to highly complex, via well-established near-net shape and selective surface net shape techniques.

For Near-Net Shape Powder Metallurgy / Hot Isostatic Pressing (NNS /PM HIP) metal powder can be supplied at the following Particle Size Distributions (at 100%) of:

<150 µm

<300 µm

<500 µm

Supply

Powders can be supplied in a range of quantities, ranging from 2.5kg, 5.0kg and 10.0kg containers up to 50kg or larger.

The following table shows the core alloys that we supply.

Group

Alloy

UNS

Similar Name

Specifications

Nickel Superalloys

Alloy 718

N07718

Inconel® 718

ASTM F3055

Alloy 625

N06625

Inconel® 625

ASTM F3056 ; AMS 7001

Alloy X/HX

N06002

Hastelloy® X


Stainless Steel

304

S30403


ASTM A276

316L

S31603

1.4404

ASTM F3184

15-5PH

S15500

1.4540

ASTM A564

17-4PH

S17400

1.4542

ASTM A56 ; AMS 7012

Alloy Steels

H13 Tool Steel

T20813


ASTM A681

Maraging 250

K92890

M250


Maraging 300

K93120

M300

ASTM A579 ; AMS 6514 ; 1.2709 ; X3NiCoMoTi 18-9-5

4140

G41400



4130

G41300



Cobalt Alloys

CoCr

R31537

CCM

ASTM F75

Alloy 6

R03006

Stellite 6; Cobalt 6b


Titanium Alloys

6Al-4V

R56400

Ti-6Al-4V Grade 5

ASTM F2924-14

6Al-4V

R56407

Ti-6Al-4V Grade 23

ASTM F3001-14

Aluminium Alloys

AlSi10Mg


DIN EN 1706:2013-12 EN AC-43000

ASTM F3318-18 ; AMS 7018

AlSiMg


F357


AlSi12Mg





  • Menu
  • Service hotline

    Service hotline

    029-89699396

  • fax

    fax

    029-89699396

  • website

    website

    www.xacti.com.cn

  • address

    address

    No.19, Zhuque street Xi’an Shaanxi

Copyright © Xi'an Aircraft Industry Titanium Industry Co., Ltd. Technical Support: 祥云平台 Disclaimers